POLYSULFIDE SEALANT
GERMAN TECHNOLOGY / MADE IN GERMANY
PGS 900TECHNICAL DATA SHEE
Insulated Glass Secondary Sealant
| TECHNICAL CHARACTERISTICS |
Two component Insulated Glass Sealant based on Polysulfide Monomers | |||
| APPEARANCE | Component A Component B |
light grey black |
||
| DENSITY | Component A Component B |
1,80 - 1,84 kg/ltr 1,62 - 1,70 kg/ltr |
||
| CORRELATION OF COMPONENTS | by weight A:B by volume A:B |
10 : 0,92 10 : 1,00 |
||
| CURING |
+/- 20% allowance of deviation (B Comp. only) Cold curing 80-100 minutes at 23°Celcius and RH 50% By temperature decrease increasing curing time and by temperature increase decreasing curing time |
|||
| POTLIFE | to be processed within 40-50 minutes by 23°Celcius and RH 50% By temperature decrease increasing potlife and by temperature increase decresing potlife. | |||
| HARDNESS | Shore A > 40 after 24 h by 23°Celcius | |||
| PACKAGING | Component A Component B Small units |
191 ltrs 19 ltrs upon request |
in steel drums in steel drums |
|
| VOLATILE CONTENT | < 1 % | |||
| MVTR (Moisture vapour transmission rate) |
6,3 gr / 24h / m² |
|||
| ARGON PENETRATION RATE |
0,0002 gr / h / m² |
|||
| GLASS-GLASS ADHESION TEST |
more than 10 minutes at 0,3 MPa |
|||
| JIG TEST | for 3 mm thickness less than 1 mm | |||
| APPLICATION |
Surfaces must be dry, clean and free of oil |
|||
| PROPERTIES |
Very good adhesion to glass, aluminium and stainless steel surfaces |
|||
| STORAGE | Guaranteed storage period is 9 months in the original packing, in dry storage facilities at temperatures between 10°Celsius and 30°Celsius Do not store under direct sun | |||
Use
IG Silicone Sealant may used with most commercially available insulating glass primary
Use
IG POLYSULFIDE SEALANT preperation may be used with most commercially available insulating glass primary sealants. The
Use
IG TPS 1000 may be used with most commercially available insulating glass primary
Use
IG HOTMELT may be used with most commercially available insulating glass primary sealants.
IG Hotmelt sealant is