PIB 2000 - PRIMARY SEALANTS - Insulating Glass

PIB 2000

PIB 2000

Use
PIB 2000& PIB 7000 G may be used with most commercially available urethane, silicone, polysulfide, or butyl hot melt insulating glass secondary sealants

Preperation
The surfaces to be bonded mu be dry, clean and free from dust and grease. Glass surfaces should be thoroughly cleaned by hand or machine with non-film forming low residue detergent and rinsed thoroughly with clean hot water.

Tech

Base Synthetic rubber (polyisobutylene), solvent-free
Color PIB 2000 (Black) / PIB 7000 G (Grey)
Consistency Solid compound
Notes Can only be applied using a heated butyl extruder

 

Performance Testing

  Typical Values Test Method
Moisture Vapor Trans-mission 0,09 g/m²/24 hr ASTM F1249+C2 3mm thickness
Argon Diffusion 0,2 L/m² /24h/ 760mm ASTM D3985        3mm thickness
Press Flow Extrusion Viscosity 13 seconds ASTM D2452 110°C (230°C) 8,6mm ofifce
Cone Penetration 55 dmm ASTM D217,150g added load
Solids Content 100% n/a
Specific Gravity 1,1 ASTM D71
Weight Per Gallon 9,2 n/a

Safety
Prior to working with this or any product consult product label and Material Safety Data Sheet (MSDS) for necessary health and safety precautions.

Storage
Store material in original unopened packaging at temperatures between 40°- 100°

  • Share:

Other products in category

PIB 7000

Use
Primary sealant PIB 7000 may be used with most commercially available urethane, silicone, polysulfide or butyl hot melt

read more
PIB 2000

Use
PIB 2000& PIB 7000 G may be used with most commercially available urethane, silicone, polysulfide, or butyl hot melt

read more
Insulating Glass contact